Z-PLA er et bionedbrydeligt glødetråd til din Zortrax 3D-printer. Brug dette materiale til at oprette komponenter med glatte, ikke-blanke overflader på dit Zortrax Inventure. Takket være dets lave krympning og minimale fordrejning kan du let 3D-udskrive store dele
Materielle egenskaber:
Ikke på lager
Advarsel: Sidste enheder på lager!
Tilgængelighedsdato:
22418
Skriv din e-mail-adresse her, hvis du vil have besked når vi igen har denne vare på lager:
Jeg ønsker en e-mail når varen kommer på lager
Buy Z-PLA and 3D print fine and detailed components with matte and smooth surfaces easily and affordably on your Zortrax 3D printer. You can process this filament on your Zortrax Inventure. The material is non-toxic, environmentally friendly, recyclable and very easy to process. With this filament you can also make large components and models, as it has little tendency to warp. Z-PLA and can be processed at low temperatures.
With this eco-friendly and recyclable material for your Zortrax 3D printer, you can easily and warp-free 3D print large models and prototypes. This is especially advantageous in architecture, mechanical engineering and medicine, where large and detailed models are often required. Let your ideas become real in a simple and cost effective way now.
With Z-PLA filament, you can 3D print easily and pleasantly. This material reduces warping and material distortion to a minimum, which is why you can easily generative manufacture large prototypes, models and components.
If PLA is so easy to process, why should I still 3D print with other filaments? Quite simple. PLA has the disadvantage that it is not very temperature and chemical resistant. You'd better use a different plastic for these requirements.
Buy Z-PLA filament and 3D print fine and detailed parts with matte and smooth surfaces easily on your Zortrax Inventure 3D printer.
Mærke | Zortrax |
Materiale | PLA |
Diameter | 1.75mm |
Farve | Grøn |
Lager | Online |
Mechanical Properties |
Metric |
Imperial |
Test Method |
Tensile Strength |
47.95 MPa |
6950 psi |
ISO 527:1998 |
Breaking Stress |
46.53 MPa |
6750 psi |
ISO 527:1998 |
Elongation at max Tensile Stress |
4 % |
4 % |
ISO 527:1998 |
Elongation at Break |
4 % |
4 % |
ISO 527:1998 |
Bending Stress |
56.80 MPa |
8240 psi |
ISO 178:2011 |
Flexural Modulus |
1.47 GPa |
213 ksi |
ISO 178:2011 |
Izod Impact, Notched |
3.14 kJ/m2 |
1.49 ft-lb/in2 |
ISO 180:2004 |
Glass Transition Temperature |
57.06° C |
135° F |
ISO 11357-3:2014 |
Melt Flow Rate |
14.48 g/10 min Load 2.16 kg Temperature 190° C |
0.0319 lb/10 min Load 4.76 lb Temperature 374° F |
ISO 1133:2006 |
Specific Density |
1.292 g/cm3 |
10.8 lb/gal |
ISO 1183-3:2003 |
Shore Hardness (D) |
79.8 |
79.8 |
ISO 868:1998 |