3DXTECH CARBONX PA6+CF GEN 3 [CARBON FIBER NYLON] 1.75mm. 1kg Black

3DXTECH 3DXTECH

CarbonX™ PA6+CF [Gen3]

CarbonX™ PA6+CF [Gen3] er fremstillet ved hjælp af en specialnylon 6 [PA6] copolymer og kulfiber med høj modul. Dette er go-to-materialet til industrielle applikationer, der kræver overlegne termiske, mekaniske og kemiske modstandsegenskaber, samtidig med at det bevarer den lethed ved udskrivning, som du er kommet til at forvente.

Flere detaljer

Ikke på lager

NYL3011000BK0

750,00 DKK

inkl. moms
750

Få besked når varen er på lager

Skriv din e-mail-adresse her, hvis du vil have besked når vi igen har denne vare på lager:

Jeg ønsker en e-mail når varen kommer på lager

Gen 3 CarbonX™ PA6+CF Carbon Fiber Reinforced Nylon

Gen 3 CarbonX™ PA6+CF filament is formulated using a PA6 copolymer reinforced with high-modulus carbon fiber. This filament is ideal for anyone that desires a structural component with high modulus, improved chemical and thermal resistance, excellent surface quality, and ease of printing. Gen3 has higher HDT than our previous grades (147°C at .45MPa) allowing for expanded use in higher-temp applications.

Unparalleled rigidity gives designers the properties they need to make their 3D printed parts with less material and save weight without sacrificing stiffness.

  • Excellent printability
  • High tensile strength and rigidity
  • Abrasion and wear resistance
  • Improved chemical resistance over traditional 3D printing materials
  • High thermal properties

Abrasive Material

This material is particularly abrasive among 3D printing filaments. Users may find standard brass nozzles are chewed through very quickly compared to standard wear and tear. When worn through, the nozzle diameter will widen inconsistently and the printer will experience extrusion issues.

Skriv bedømmelse

Skriv bedømmelse

Filament Specifications:

1.75mm and 2.85mm +/- 0.05mm in diameter

Recommended Print Settings:

  • Extruder: 240-270°C
  • Bed Temp: 80-110°C
  • Nozzle: We currently recommend a hardened steel nozzle with a minimum diameter of 0.4mm
  • Other: Ideal layer height is 60% of nozzle diameter. We do not recommend printing layers smaller than 0.2mm with carbon fiber reinforced filaments.
  • Bed Prep: Magigoo Bed Prep Adhesive gives us the best results
  • Heated Chamber: Not required, but a heated chamber between 30-80°C allows for superior layer bonding and mechanical properties
  • Supports: Water soluble AquaTek X1 USM works great for complex parts.
  • Drying Instructions: 90°C for 4 hours.